| Property |
Test Method |
Value |
Unit |
| GRP |
GRV |
GRE |
| Ultimate Hoop Stress-Rupture |
ASTM D 1559 |
570 |
570 |
570 |
M Pa |
 |
| Hydrostatic Design Basis (Uni-axial) |
ASTM D 2992 B |
350 |
350 |
- |
M Pa |
|
| Hydrostatic Design Basis (Bi-axial) |
ASTM D 2992 B |
138 |
138 |
172 |
M Pa |
|
| Hydrostatic Design Stress (Uni-axial) |
ASTM D 2992 B |
175 |
175 |
- |
M Pa |
|
| Hydrostatic Design Stress (Bi-axial) |
ASTM D 2992 B |
68 |
68 |
87 |
M Pa |
| Property |
Test Method |
Value |
Unit |
| GRP |
GRV |
GRE |
| Axial Tensile Stress |
ASTM D 2105 |
35 |
50 |
75 |
M Pa |
|
| Axial Tensile Modulus |
ASTM D 2105 |
13000 |
13000 |
15000 |
M Pa |
|
| Hoop Tensile Stress |
ASTM D 2290 |
250 |
250 |
300 |
M Pa |
|
| Hoop Tensile Modulus |
ASTM D 2290 |
24000 |
24000 |
30000 |
M Pa |
|
| Hoop Bending Modulus |
ASTM D2415 |
25000 |
25000 |
25000 |
M Pa |
|
| Pisson's Ration [Hoop loading] |
- |
0.45 |
0.45 |
0.45 |
- |
|
| Poisson's Ratio [Axial loading] |
ASTM D 2412 |
0.65 |
0.65 |
0.65 |
- |
| Property |
Value |
Unit |
| GRP |
GRV |
GRE |
| Coefficient of Linear Thermal Expansion |
20X10E-6 |
20X10E-6 |
20X10E-6 |
M Pa |
|
| Specific Gravity |
1.8 |
1.8 |
1.8 |
- |
|
| Glass content (by weight) |
65 |
65 |
70 |
% |
|
| Hazen William Coefficient |
150 |
150 |
150 |
- |
|
| Maximum Temperature |
60 |
90 |
110 |
°C |
|
| Thermal Conductivity |
0.3 |
0.3 |
0.3 |
W/m-K |
|
| Roughness factor (Including head loss over joints) |
0.04 |
0.04 |
0.04 |
mm |
|
| Effective Roughness (only pipe) |
0.0015 |
0.0015 |
0.0015 |
mm |
|
Bi-axial values - 55 Deg. Winding angle
Uni-axial values - 63 Deg. Winding angle
|
|